This document specifies a test method for determining the polytypes and their ratios in silicon carbide (SiC) wafers or bulk crystals using ultraviolet photoluminescence (UVPL) imaging. The range of SiC is limited to semiconductor SiC doped with nitrogen and boron to have a deep acceptor level and a shallow donor level, respectively. The SiC wafers or bulk crystals discussed in this document typically show electrical resistivities ranging from 10−3 ohm · cm to 10−2 ohm · cm, applicable to power electronic devices.

This method is applicable to the SiC-crystal 4H, 6H and 15R polytypes that contain boron and nitrogen as acceptor and donor, respectively, at concentrations that produce donor-acceptor pairs (DAPs) to generate UVPL. In 4H-SiC the boron and nitrogen concentrations typically range from 1016 cm−3 to 1018 cm−3. Semi-insulating SiC is not of concern because it usually contains minimal boron and nitrogen; therefore deep level cannot be achieved.


Informations générales

  • État actuel :  Publiée
    Date de publication : 2021-02
  • Edition : 1
  • :
    ISO/TC 206
    Céramiques techniques
  • 81.060.30
    Céramiques techniques avancées

Acheter cette norme

Format Langue
PDF + ePub
Papier
  • CHF138

Vous avez une question?

Consulter notre FAQ

Service à la clientèle
+41 22 749 08 88

Horaires d’ouverture:
De lundi à vendredi - 09:00-12:00, 14:00-17:00 (UTC+1)

Suivez l'actualité de l'ISO

Inscrivez-vous à notre Newsletter (en anglais) pour suivre nos actualités, points de vue et informations sur nos produits.