This document describes a pulse propagation method for determining the storage component of the complex tensile modulus E' of polymers at discrete frequencies typically in the range 3 kHz to 10 kHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 10 kHz. With materials having a higher loss, significant errors in velocity measurement are introduced through decay of amplitude.

The method allows measurements to be made on thin films or fine fibres and long specimens, typically tapes of 300 mm × 5 mm × 0,1 mm or fibres of 300 mm × 0,1 mm (diameter).

This method may not be suitable for cellular plastics, composite plastics and multilayer products.


Общая информация

  • Текущий статус :  Published
    Дата публикации : 2019-04
  • Версия : 2
    Число страниц : 8
  • :
    ISO/TC 61/SC 5
    Physical-chemical properties
  • 83.080.01
    Plastics in general

Приобрести данный стандарт

Формат Язык
PDF + ePub
Бумажный
  • CHF58

Жизненны цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах