ISO 21813 specifies methods for the chemical analysis of fine high purity barium titanate powders used as the raw material for fine ceramics.

ISO 21813 stipulates the determination methods of the barium, titanium, aluminium, cadmium, calcium, cobalt, dysprosium, iron, lead, magnesium, manganese, nickel, niobium, potassium, silicon, sodium, strontium, vanadium, zirconium, carbon, oxygen and nitrogen contents in high purity barium titanate powders. The barium and titanium contents, the major elements, are determined by using an acid decomposition-gravimetric method or an acid decomposition-inductively coupled plasma-optical emission spectrometry (ICP-OES) method. The aluminium, cadmium, calcium, chromium, cobalt, dysprosium, iron, lead, magnesium, manganese, nickel, niobium, potassium, silicon, strontium, vanadium and zirconium contents are simultaneously determined via an acid digestion-ICP-OES method. The nitrogen content is determined by using an inert gas fusion-thermal conductivity method, while that of oxygen is determined via an inert gas fusion-IR absorption spectrometry method. Finally, the carbon content is determined using a combustion-IR absorption spectrometry method or a combustion-conductometry method.


Общая информация

  • Текущий статус :  Published
    Дата публикации : 2019-02
  • Версия : 1
    Число страниц : 25
  • :
    ISO/TC 206
    Fine ceramics
  • 81.060.30
    Advanced ceramics

Приобрести данный стандарт

Формат Язык
PDF + ePub
Бумажный
  • CHF118

Жизненны цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

  • Сейчас
    ISO 21813:2019

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах