This document specifies a method for the determination of the particle size distribution of coating powders by sieve analysis. Particle size distributions with a maximum of less than 100 µm is determined by laser diffraction, ISO 8130‑13. This method is used especially for determining the oversize material or for the presence of contamination and can be used as a quality control procedure ("go"/"no go" test) by checking the amount retained on a single sieve.

The following particle sizes are typical for coating powders, however the particle size can deviate depending on the application:

— thin-film technology: 1 µm to 63 µm;

— electrostatic coating: 10 µm to 200 µm;

— fluidizing-bed method: 100 µm and above.

NOTE Sieves with a mesh size smaller than 32 µm are not practical and are likely to become blind during use.


Общая информация

  • Текущий статус :  Published
    Дата публикации : 2019-04
  • Версия : 2
  • :
    ISO/TC 35/SC 9
    General test methods for paints and varnishes
  • 87.040
    Paints and varnishes

Приобрести данный стандарт

Формат Язык
PDF + ePub
Бумажный
  • CHF58

Жизненный цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах.