ISO 13947:2007 specifies a metallographic method for determining the non-metallic inclusion level in metal powders using a powder-forged specimen. The test method covers repress powder-forged test specimens in which there has been minimal lateral flow (< 1 %). The core region of the powder-forged test specimen contains no porosity detectable at 100X magnification.

This test method can also be used to determine the non-metallic inclusion content of powder-forged steel parts. However, in parts where there has been a significant amount of material flow, the near-neighbour separation distance needs to be changed, or the inclusion sizes agreed between the parties need to be adjusted.

This test method is not suitable for determining the non-metallic inclusion level of parts that have been forged such that the core region contains porosity. At the magnification used for this test method, residual porosity is hard to distinguish from inclusions. Too much residual porosity makes a meaningful assessment of the inclusion population impossible.


Общая информация

  • Текущий статус :  Withdrawn
    Дата публикации : 2007-02
  • Версия : 1
  • :
    ISO/TC 119/SC 2
    Sampling and testing methods for powders (including powders for hardmetals)
  • 77.160
    Powder metallurgy

Жизненны цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

  • В настоящее время отменен
    ISO 13947:2007
  • Пересмотрен
    ISO 13947:2011

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах