ISO 22889:2007

Metallic materials -- Method of test for the determination of resistance to stable crack extension using specimens of low constraint

ISO 22889:2007 specifies methods for determining the resistance to stable crack extension in terms of crack opening displacement and critical crack tip opening angle for homogeneous metallic materials by the quasistatic loading of cracked specimens that exhibit low constraint to plastic deformation. Compact and middle-cracked tension specimens are notched, precracked by fatigue, and tested under slowly increasing displacement.

ISO 22889:2007 describes methods covering tests on specimens not satisfying requirements for size-insensitive fracture properties; namely, compact specimens and middle-cracked tension specimens in relatively thin gauges.

Methods are given for determining the crack extension resistance curve. Methods for determining point values of fracture toughness for the middle-cracked tension specimen are also given.


Общая информация

  • Текущий статус :  Withdrawn
    Дата публикации : 2007-12
  • Версия : 1
  • :
    ISO/TC 164/SC 4
    Fatigue, fracture and toughness testing
  • 77.040.10
    Mechanical testing of metals

Жизненны цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

  • В настоящее время отменен
    ISO 22889:2007
  • Пересмотрен
    ISO 22889:2013

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах

 Subscribe