ISO 11125-3:1993

Preparation of steel substrates before application of paints and related products -- Test methods for metallic blast-cleaning abrasives -- Part 3: Determination of hardness

Specifies a test method for the determination of the Vickers hardness (using a test force of 9,807 N, i.e. HV 1, when testing particles with a diameter greater than 0,5 mm, and a test force of 4,904 N, i.e. HV 0,5, when testing particles with a diameter of 0,3 mm to 0,5 mm). The method is not recommended for the testing of particle sizes below 0,3 mm. The purpose is to establish the soundness of the metallic abrasive. Significant levels of internal shrinkage or hollow particles will reduce the apparent density. Annex A gives information on the international standards series for metallic blast-cleaning abrasives ISO 11124 and ISO 11125.


Общая информация

  • Текущий статус :  Withdrawn
    Дата публикации : 1993-12
  • Версия : 1
  • :
    ISO/TC 35/SC 12
    Preparation of steel substrates before application of paints and related products
  • 25.220.10
    Surface preparation

Жизненны цикл

Стандарт, который пересматривается каждые 5 лет



Изменения / Исправления

  • В настоящее время отменен
    ISO 11125-3:1993
  • Пересмотрен
    ISO 11125-3:2018

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

Будьте в курсе актуальных новостей ИСО

Подписывайтесь на наши новости, обзоры, а также на информацию о продуктах

Subscribe