ISO 9327-3:1999
1999-06
ISO 9327-3:1999
Тезис
1.1 This part of ISO 9327 applies to forgings and rolled or forged bars in thicknesses up to 50 mm manufactured
from the steels listed in Table 1 and to be delivered according to the specifications given in ISO 9327-1.
1.1 This part of ISO 9327 covers the following data:
a) in Table 1 the limits for
the chemical composition according to the cast analysis;
the tensile properties at room temperature;
the indications on the usual heat treatment condition at the time of delivery;
b) in Table 2 the permissible product analysis tolerances on the limiting values given for the cast analysis;
c) in Table 3 the minimum impact energy values.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 1999-06Этап: Международный стандарт подлежит пересмотру [90.92]
-
Версия: 1
-
Технический комитет :ISO/TC 17/SC 10
- RSS обновления
Новая версия в процессе разработки
ISO/DIS 9327-3
ISO/DIS 9327-3
Steel forgings and rolled or forged bars for pressure purposes — Technical delivery conditions
Part 3: Nickel steels with specified low temperature properties
ISO/DIS 9327-3
Жизненный цикл
-
Ранее
ОтозваноISO 2604-1:1975
-
Сейчас
ОпубликованоISO 9327-3:1999
Стандарт, который пересматривается каждые 5 лет
Этап: 90.92 (Будет пересмотрено)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
-
Будет заменено
В стадии разработкиISO/DIS 9327-3